Etude par analyse XPS et microscopie électronique des microprofils développés lors de l'altération expérimentale dans l'eau douce de verres basaltiques et andésitiques

Résumé En Fr

The experimental alteration in water at 90°C of an andesitic glass and two basaltic ones has been investigated via X-ray photoelectron spectrometry (XPS) and electron microscopy. At the beginning of the reaction, the hydration of glass and the ion exchange with H+ of the solution take place. After a few days, one notices the growth of a superficial Fe-bearing layer. After one month duration, this layer becomes either non sticking (basaltic glasses) or sticking on the surface (ande¬ sitic glass) : it is made of iron-bearing phases, amorphous or poorly crystallized (ferrihydrite) . In all cases, a growth of sepiolite occurs at the interface preci¬ pitate-solution and, for the iron-richest glass, iron phyllosilicates growth in the inner part of the alteration layer.

L'altération expérimentale dans l'eau douce à 90°C d'un verre andésitique et de deux Verres basaltiques artificiels a été étudiée par spectrométrie XPS et microscopie électronique. Au début de l'interaction, l'hydratation du verre et l'échange d'ions avec les H+ de la solution prédominent. Après quelques jours, on note la croissance d'une couche superficielle très enrichie en fer ; au bout d'un mois, cette couche devient faiblement adhérente (verres basaltiques) ou reste au contraire fixée au substrat (verre andésitique) ; il s'agit de phases ferrifères amorphes ou mal cristallisées (ferrihydrite) . Parallèlement, se forme dans tous les cas de la sépiolite à l'interface précipité-solution et, dans le cas du verre le plus riche en fer, des phyllosilicates ferrifères localisés à l'intérieur du microprofil d'altération.