Sur la formation d'argiles chromifères

Résumé En Fr

Due to non-reactivity of chromium (III) ions directly with Si (OH)4 in solution, we have investigated their incorporation in a synthetic magnesium clay. It can be shown that the crossed lattice of a clay mineral germinates only when the molecular ratio MgO/C2O3 is either equal or higher than 5. At concentrations more than the said value, Cr (III) ions hinder the formation of a crossed lattice and impose a spinel structure. ..for the ratio MgO/Cr2O3 equal to 100 in solution, the X-ray diffraction diagram the synthetic product is -well defined, 5.85 % of Cr2O3 is found on chemical of the analysis, which is close to those of natural chromiferous clay minerals. Dissolution in N/50 HCl of the synthesized substance shows that an important part of chromium is fixed in the lattice, essentially in the octahedric cavity of the sheet.

Les ions chrome (III) ne pouvant réagir directement avec les molécules simples Si (OH)4 d'une solution, nous avons étudié leur incorporation dans une argile magnésienne synthétique. On montre qu'un réseau croisé de phyllite ne prend naissance que pour des rapports molaires MgO/Cr2O3 en solution égaux ou supérieurs à 5. A concentration plus élevée, le cation Cr3+ empêche la formation du réseau croisé et impose une structure spinelle aux ions Mg2+. Pour un rapport MgO/C2O3 dans la solution égal à 100, le diffrac to gramme des rayons X présente des raies nettes. L'analyse chimique du produit synthétisé dans ces conditions donne un pourcentage de 5,85 % en Cr2O3, teneur voisine de celle des phyllites naturelles. On assiste à un enrichissement du solide en chrome à partir de la solution. Des essais de dissolution du produit dans HCl N/50 montrent qu'une proportion assez importante du chrome s'est fixée dans le réseau, essentiellement dans les cavités octaédriques du feuillet phylliteux.