Etude de l'influence des complexants de l'aluminium et du broyage des hydroxydes d'aluminium sur la formation hydrothermale de la kaolinite

Résumé En Fr

We have studied the synthesis of kaolinite from crys-tallized aluminum hydroxide and amorphous silica in a domain of temperature between 125°C and 200°C. The aluminous clay mineral does not appear after a week's treatment of the mixture (molar ratio Si/Al = 1) at 200°C . But in the presence of organic aluminum complexing acids, aluminum becomes more rapidly mobile and kaolinite forms even at a temperature lower than 200°C. Reducing the size of the original hydroxide particles also lowers the temperature of synthesis. The reaction still takes place at 135°C which is the lower limit temperature for the transformation of gibbsite into boehmite.

Nous avons étudié la synthèse de la kaolinite à partir d'hydroxyde d'aluminium cristallisé et de silice amorphe dans un domaine de température compris entre 125°C et 200°C. Quand on traite un tel mélange (rapport molaire Si/Al = 1) à 200°C pendant une semaine, la phyllite alumineuse ne se forme pas. Par contre, lorsqu'on opère en présence d'acides organiques complexants de l'aluminium, celui-ci est mobilisé plus rapidement et la kaolinite se forme même à une température inférieure â 200°C. En diminuant la taille des particules de l'hydroxyde de départ, on abaisse aussi la température de synthèse. La réaction a encore lieu à 135°C, température limite inférieure de transformation de la gibbsite en boehmite.