Le magnétisme des céramiques anciennes

Résumé En Fr

A method of studying fired clay and potsherds has been developped, using magnetization measurements and Mossbauer spectrometry, which are only sensitive to the iron they contain. Using this magnetic method, pottery of ancient Iran has been compared with a standard clay fired at different temperatures under controlled conditions of oxidation and reduction. Magnetic groups of sherds have been observed, and are related with same firing conditions ; they were used to characterize potter kilns or hearths : - complete oxidation and high ( 1100°C) temperature, for the Ubaid tradition "buff" pottery, - complete reduction and moderate ( 950°) temperature, for the Tepe Hissar II or III light grey pottery, - mainly reduction and low ( 75O°C) temperature for the Tureng Tepe II or III black grey pottery, - mixing oxidation and reduction, with moderate ( 950° C) temperature, in neolithic hearths, for the red ware of Tureng Tepe II or Tape Hissar II.

Des fours et foyers de potiers de l'Iran ancien ont pu acre caractérisés par le magnétisme de la poterie qu'ils ont produite : les mesures magnétiques et les spectres Hossbauer des tessons étudiés ont été comparés avec ceux d'une terre à poterie de référence, cuite dans différentes conditions. Ont ainsi été caractérisés : - des fours oxydants, à haute température !100aC, produisant une céramique jaune clair de tradition obsidienne, - des fours réducteurs, à température moyenne 950°C, produisant une céramique gris clair du type Tepe Hissar II et III, - des fours réducteurs à basse température 750°C, produisant une céramique gris noir du type Tureng Tepe II et III, - des foyers néolithiques, à atmosphère mixte et à température inférieure à 950°C, produisant une céramique rouge du type Tureng Tepe II ou Tepe Hissar II.