Apport de l'analyse statistique des produits de corrosion à la compréhension des processus de dégradation des bronzes archéologiques

Résumé En Fr

The analysis of the corrosion products of three single phase bronzes, representative of a corpus of Bronze Age objects, was conducted by X-ray microanalysis on a scanning electron microscope. The variations of the main chemical species found in the corrosion products have been characterized. A growth model is suggested to explain the two main corrosion structures observed on archaeological bronzes. The selective dissolution ofthe copper from the alloy can occur via two mechanisms controlled by mass transfer one in relation with the copper cations, and the other one which is dependent on the diffusion of anionic species. A stationnary state is probably reached few decades after the burial. Then, the corrosion process can evoluate locally.

L'analyse élémentaire des composés de corrosion de trois bronzes monophasés, représentatifs d'un corpus d'objets de l'Age du Bronze, a été effectuée par microanalyse X sur microscope électronique à balayage. Les variations des teneurs des principaux éléments chimiques dans les couches de corrosion ont été caractérisées. Un modèle de formation des deux principales structures de corrosion des bronzes archéologiques enfouis est proposé. La dissolution sélective du cuivre de Palliagc peut être contrôlée par deux types de processus de transport : l'un, par les cations du cuivre issus de l'oxydation de l'alliage, l'autre par les espèces anioniques de l'électrolyte du sol. Un état stationnaire est probablement atteint après des durées d'enfouissement de quelques dizaines d'années. La corrosion n'évolue alors que localement sur l'objet.