Influence des écarts à la composition sur les propriétés magnétiques des phases Mn3 Ga C1˗x et Mn5 Si3 Cx

Résumé En Fr

It has been shown that Mn₅Si₃ type silicides dissolve amounts of small non metals. When the octaedral holes of Mn5Si3 are partially filled with carbon, this compound has magnetic properties under 152° K. The ferromagnetic and dilatometric properties are very sensitive to non stoichiometry. Mn₃GaC₁₋ₓ, is a perowskite type carbide. It presents an antiferro-ferromagnetic transition at 150° K. This transformation is strongly dependent of non stoichiometry. When the formula has a value betwen Mn₃GaC₀,₉₈ and MnGaC₀,₉₅ a new type of magnetic transformation appears. There is no magnetic transformation when the formula has a value between Mn₃GaC₀,₉₅ and Mn₃GaC₀,₅₅. This work includes dilatometric study of the transitions, and the effect of various magnetic fields on the thermomagnetic curves.

Le remplissage partiel des sites octaédriques de Mn₅Si₃ par des atomes de carbone fait apparaître des propriétés ferromagnétiques à basses températures. Les propriétés, magnétiques ainsi que les propriétés dilatométriques sont très sensibles aux écarts de composition. Mn₃GaC présente une transition antiferro-ferromagnétique à 150° K. Cette transition est modifiée profondément par de faibles écarts à la composition en carbone. Entre Mn₃GaC₀,₉₈ et Mn₃GaC₀,₉₅, un nouveau type de transition magnétique apparaît. Lorsque la formule est comprise entreMn₃GaC₀,₉₅ et Mn₃GaC₀,₅₅, le composé ne présente plus de transition. Les deux types de transition sont étudiés sous différentes valeurs du champ magnétique appliqué, l'étude dilatométrique montre également la différence fondamentale entre les deux types de transition.