Étude structurale de Ca Ge N2 et Ca1˗xGe N2

Résumé En Fr

The structural study of CaGeN₂> shows that the latter crystallises in the tetragonal system with a = 5.42₆ Å and c = 7.154 Å. The space group is I[-4]2d. The structure is formed by a sequence of tetrahedrons, Ge-4N, analogous to that of Si-4O tetrahedrons of the β-cristobalite. The Ca atoms are localised in the insterstices of the lattice and are tetrahedrally surrounded by the N atoms. The series of compounds Ca₁₋ₓGeN₂ is prepared through a selective action of O₂ on the Ca atoms ; this leaves the tetrahedral skeleton Ge-4N untouched. A variation of the parameters is observed. The space group is preserved, the Ca atoms filling the sites defined above at random.

L'étude structurale de CaGeN₂ montre que celui-ci cristallise dans le système quadratique avec a = 5,42₆ Å et c = 7,154 Å ; le groupe spatial est I[-4]2d. La structure consiste en un enchaînement de tétraèdres Ge-4N analogue à celui des tétraèdres Si-4O de la cristobalite ß. Les atomes de Ca se trouvent dans les cavités de ce réseau, et sont entourés tétraédriquement par les atomes d'azote. Une série de composés Ca₁₋ₓGeN₂ est obtenue par l'action sélective de l'oxygène sur le calcium qui laisse intact le squelette tétraédrique Ge-4N. On observe une variation des paramètres. Le groupe spatial est conservé, l'atome de Ca occupant statistiquement le site précédemment défini.