Évolution des structures cristallographique et magnétique des solutions solides ilménite˗hématite

Résumé En Fr

Similary to the case of the solid solution FeTiO₃-αFe₂O₃, the series NiTiO₃-αFe₂O₃ manifests a crystallographic transition R[-3]—R[-3]c which depends strongly on the quench temperature. Presentation of a magnetic model which covers whole solid solution range of ilmenite-hematite. The resulting magnetic moment is correlated to the composition and degree of cationic order of the solution. For the series FeTiO₃-αFe₂O₃, the agreement is excellent, between the calculated order ratio obtained from the magnetic measurements of Y. Ishikawa and neutron-diffraction data of G. Shirane.

Comme pour la solution solide FeTiO₃-αFe₂O₃, la série NiTiO₃-αFe₂O₃ présente une transition cristallographique R[-3]-R[-3]c qui dépend fortement de la température de trempe. Nous élaborons un modèle magnétique qui relie, pour toutes les solutions solides ilménite˗hématite, le moment magnétique résultant à la composition et au degré d'ordre cationique. Pour la série FeTiO₃-αFe₂O₃, l'accord est excellent entre le calcul du degré d'ordre à partir des mesures magnétiques de Y. Ishikawa et les mesures de diffraction neutronique de G. Shirane.