Spectroscopie Raman dans le système ZrO2-M2O3 (M = Sc, Yb)

Résumé En Fr

A Raman spectroscopic study of the ordered γ and δ phases, and the disordered cubic phase, is presented for the system ZrO₂ — Sc₂O₃. The order-disorder (γ to cubic) transition is studied by compositional variation in the solid solution Zr₅Sc[2-x]CYb[x]O₁₃. This transition is also shown at 750 °C for the composition Zr₅Sc₁,₈Yb₀,₂ O₁₃. The importance of renormalisation of spectra obtained at high temperatures is discussed. The T[2θ] mode of the vacancy free cubic phase is found in the γ phase, where cations are present in octahedral coordination to oxygen. This study shows that in the « ordered » phases, a residual disorder persists in the distribution of the oxygen vacancies, which becomes more important as the cubic phase is approached.

Nous présentons une étude par diffusion Raman des phases ordonnées γ et δ ainsi que de la phase cubique de composés du système ZrO₂ — Sc₂O₃. La transition ordre-désordre (γ → cubique) est étudiée par variation de la composition dans la solution solide Zr₅Sc[2-x]CYb[x]O₁₃. Cette transition est aussi mise en évidence à 750 °C sur le composé Zr₅Sc₁,₈Yb₀,₂ O₁₃. L'intérêt d'une renormalisation des spectres de haute température est montré. Le mode T[2θ] de la phase cubique non lacunaire est retrouvé en phase γ où subsistent des cations octacoordonnés à l'oxygène. Ce travail montre que dans les phases « ordonnées » il persiste un désordre résiduel dans la distribution lacunaire, qui est d'autant plus important que l'on se rapproche de la phase stabilisée.