Etude expérimentale de la distribution du fer ferreux et du magnésium entre spinelle chromifère et bain silicaté basique

Résumé En Fr

At one atmosphere total pressure, at temperatures of 1180-1300 °C and oxygen fugacities of 10-9-10-3 atm, the parition of ferrous iron and magnesium between chromian spinel and basic silicate melt is controlled mainly by the ferrous iron content and the magnesium content of the liquid. The partition coefficient varies between 1.5 and 6 for ferrous iron and between 1 and 2 for magnesium. The trivalent cations of spinel have a little influence on that partitioning : the magnesium content of spinel increases with the aluminium content. Temperature and oxygen fugacity interfere when their variations induce a modification of the ferrous iron content of the liquid (variation of the Fe2+/Fe3+ ratio), or a modification of the magnesium content of the liquid (due to the crystallization of olivine or pyroxene).

A pression atmosphérique, pour des températures de 1180 à 1300 °C et des fugacités d'oxygène de 10-9 à 10-3 atm, la distribution du fer ferreux et du magnésium entre spinelle chromifère et liquide silicaté de composition tholéiitique est gouvernée principalement par les teneurs en fer ferreux et en magnésium du liquide. Le coefficient de distribution varie de 1,5 à 6 pour le fer ferreux et de 1 à 2 pour le magnésium. Les cations trivalents du spinelle ont aussi une influence : le spinelle est d'autant plus magnésien qu'il est plus alumineux. Température et fugacité d'oxygène interviennent indirectement, dans la mesure où leurs variations conduisent à une modification des teneurs en fer ferreux (variation du rapport Fe2+/Fe3+) ou en magnésium (cristallisation de ferromagnésiens) dans le liquide.