Non-Invasive Raman Classification Comparison with pXRF of Monochrome and Related Qing Porcelains: Lead-Rich-, Lead-Poor-, and Alkali-Based Glazes
Fiche du document
18 juillet 2024
- ISIDORE Id: 10670/1.3e6cb5...
- hal: hal-04654791
- doi: 10.3390/ma17143566
- PUBMED: 39063858
- PUBMEDCENTRAL: PMC11278898
Ce document est lié à :
info:eu-repo/semantics/altIdentifier/doi/10.3390/ma17143566
Ce document est lié à :
info:eu-repo/semantics/altIdentifier/pmid/39063858
http://creativecommons.org/licenses/by/ , info:eu-repo/semantics/OpenAccess
Mots-clés
Pb content China glaze monochrome porcelain composition Qing Dynasty Raman pXRF non-invasive classificationSujets proches
Chinaware China (Porcelain) Knowledge, Classification of porcelainCiter ce document
Philippe Colomban et al., « Non-Invasive Raman Classification Comparison with pXRF of Monochrome and Related Qing Porcelains: Lead-Rich-, Lead-Poor-, and Alkali-Based Glazes », HAL SHS (Sciences de l’Homme et de la Société), ID : 10.3390/ma17143566
Métriques
Partage / Export
Résumé
Chinese porcelain with an optically clear colored glaze, imported to Europe from the Kangxi period (1662–1722, Qing Dynasty) onwards was highly collected by the French Elite of the 18th century. The bright colors with a clear, shiny glaze were unlike anything produced in Europe at that time. The colors of enamelled artifacts (on biscuits or already glazed porcelain) can be fully monochrome or consist of associations of large monochromatic areas with or without application of gilding. Non-invasive portable XRF and mobile Raman analyses have previously shown their effectiveness in the characterization of (colored) glassy silicates. In this study, we compare the Raman signatures of twenty-one Chinese artifacts fully—or with major monochrome area (sancai)—decorated with blue, turquoise (or celectian blue), honey-yellow, green, eggplant, and red color. Different types of glazes are identified and confirmed by pXRF: lead-rich, lead-poor-alkali, lead-doped alkali, and alkali-based compositions. However, an unexpected low level of lead is observed in the turquoise glazes, likely to optimize the gloss. Raman spectroscopy appears more reliable to compare the Pb content than pXRF. This work presents Raman spectral signatures of glazes that can potentially be used for non-invasive object classification and counterfeit detection.