The influence of the constituent elements on the corrosion mechanisms of silver alloys in sulphide environments: the case of sterling silver
Fiche du document
31 mai 2017
- handle: 10670/1.3qg9bu
- hal: hal-02426459
- doi: 10.1039/c7ra02330h
Ce document est lié à :
info:eu-repo/semantics/altIdentifier/doi/10.1039/c7ra02330h
info:eu-repo/semantics/OpenAccess
Sujets proches
SpecieCiter ce document
Isabel Tissot et al., « The influence of the constituent elements on the corrosion mechanisms of silver alloys in sulphide environments: the case of sterling silver », HAL-SHS : histoire de l'art, ID : 10.1039/c7ra02330h
Métriques
Partage / Export
Résumé
The corrosion of copper and silver in sulphide environments was assessed by several analytical techniques to investigate the influence of each one on the corrosion of sterling silver. The surface colour changes with the immersion time due to the formation of corrosion products composed of particles with distinct sizes and shapes and the consequent layer thickening. Ag 2 S is the main corrosion product of silver. At early stages of corrosion, Cu develops Cu 2 O and Cu 2 S, and later Cu 2 O again. After the corrosion of sterling silver, pure Cu and Ag are compared, and the predominant influence of Cu at the first stages may be suggested whilst Ag mainly contributes to longer corrosion stages. The layer-by-layer corrosion structure observed for the sulphidation of sterling silver was not observed for its constituent elements.